Silica fume is also referred to as micro silica or condensed silica fume but the term silica fume has been generally accepted
The addition of ultra fine particles in concrete improves strength of concrete
The optimum proportion of silica fume is found in between 20% and 25% by weight of concrete
Silica Fume when react with calcium hydroxide on hydration of cement produces calcium siicate hydrate which has good binding properties.


1 Physical Properties
Diameter is about 0.1 µ to 0.2 µ
Surface area about 30,000 m²/kg
Density varies from 150 to 700 kg/m³
When its density is about 550 kg/m³ it is the best suited as concrete additive

2 Chemical Composition
Contains more than 90 percent silicon dioxide
Other constituents are carbon, sulphur and oxides of aluminium, iron, calcium, magnesium, sodium and potassium


1 Properties of Fresh Concrete
Too much silica fumes cause the concrete to become sticky and thus reduces the workability
Silica fume addition up to 15% by weight of cement does not result in any loss of workability
Silica fume concrete, due to larger surface area of fine particle requires higher water content for same workability than ordinary concrete


Resistance to Chemical Attack
Silica fume checks sulphate attack by
Being very fine, it reduces permeability and the entry of sulphate ions.
By consuming the calcium hydroxide in course of pozzolanic action, it checks conversion of mono-sulphoaluminate into ettringite.


Silica fume improves the properties of fresh and hardened concrete
Fresh concrete made with silica fume is more cohesive
Silica fume reduces segregation and bleeding
Silica fume improves the durability of concrete
Lack of bleeding allows a more efficient finishing process


The use of silica fume give rise to an increase in the fresh as well as hardened properties of concrete, with less cement and a concrete having better resistance for freezing and thawing than ordinary concrete

Durability is improved through significant improvement in resistance to chemical attack. The chief reasons for this are reduced permeability and reduced levels of calcium hydroxide

Reinforcement corrosion is vastly reduced due to improved permeability, increased resistivity and improved tensile strength.
Post: #2
The use of pozzolanic materials is an old as that of the art of concrete construction. It was recognized long time age, that the suitable pozzolona used in appropriate amount, modify certain properties of fresh and hardened mortars and concretes.
It has been amply demonstrated that the best pozzolona in optimum proportions mixed with Portland cement improves many qualities of concrete, such as:
• Lower the heat of hydration and thermal shrinkage ;
• Increase the water tightness;
• Reduce the alkali- aggregate reaction;
• Improve resistance to attack by sulphate soils and sea water;
• Improve workability;
• Lower costs.
Pozzolanic materials are siliceous or siliceous and aluminous materials, which in themselves possess little or no cementitious value, but will, in finely divided form and in the presence of moisture, chemically react with calcium hydroxide liberated on hydration, at ordinary temperature, to form compounds, possessing cementitious properties.
Silica fume is a by-product from electric arc furnaces used in the manufacture of silicon metal of silicon alloys. The material, which contains more than 80% silica in the form of extremely fine particles (0.1 µm average diameter). When used to produce high-performance concrete, silica fume is typically 4-15% of the cement weight. The exact addition rate depends on the specific performance characteristic to be improved. Compared to the other ingredients in concrete, the amount of silica used is small.
For the silica fume to be effective, there are two issues that must be known:
• First, the agglomerations that make up the densified silica must be broken down.
• Second the silica fume must be distributed uniformly throughout the concrete.
 Silica fume must always be added with the coarse aggregate and some of the
Water. Never batch the silica fume alone or first into the mixer. Mix these materials for 11/2 minutes.
 Add the Portland cement and any other cementitious material such as fly ash or
Slag cement. Mix for an additional 11/2 minutes.
 Add the fine aggregate and use the remaining water to wash in any chemical admixtures. Mix for 5 minutes, rest for 3 minutes, and mix for 5 minutes. Actual time of mixing may vary, depending upon the characteristics of mixer. If full dispersion and efficient mixing has been accomplished, mix longer.
Silica fume works on chemical reaction called the "pozzolanic" reaction. The hydration (mixing with water) of Portland cement produces many compounds, including calcium silicate hydrates (CSH) and calcium hydroxide (CH). The CSH gel is known to be the source of strength in concrete. When silica fume is added to fresh concrete it chemically reacts with the CH to produces additional CSH. The benefit of this reaction is twofold; increased compressive strength and chemical resistance. The bond between the concrete paste and the coarse aggregate, in the crucial interfacial zone, is greatly increased, resulting in compressive strengths that can exceed 1046Kg/cm2. The additional CSH produced by silica fume is more resistant to attack from aggressive chemicals then the weaker CH.
Chemical composition of silica fume will mostly depend upon composition of the principle product being made by furnace additionally, the composition is also influenced by the furnace design; generally a furnace with a heat recovery system produces silica fume with lower ignition loss. The sio2 content of silica fume varies with the silica content of alloy being producer. Unlike other by product pozzolona such as fly ash, silica fume from a single source is little or no variation in chemical composition from one day to another,
Item Requirement (%)
SiO2 97.6
Al2O3 0.70
Fe2O3 0.28
CaO 0.30
MgO 0.50
K2O 0.80
Na2O 0.26
The specific gravity of calcium silicate fluoride (CSF) from silicon metal of ferrosilicon alloy industries is close to that of amorphous silica that is approximately 2.2
The amorphous silica structure and the fine particle size are the principle reasons for the excellent pozzolanic activity of CSF, the surface area by Blaine’s air permeability method ranged from about 3.3 to 7.7 m2 / g. The spherical shape of CSF can be confirmed by scanning electron microscopy of well- dispersed particles. Generally, the particles exist in the form of agglomerates.
Scanning Electron Micrograph of silica fume particles.
Water demand increases in proportion to the amt of silica fume added. The increase in water demand of concrete containing silica fume is about 1% for every 1% cement substituted Workability is the ease with which a concrete mix can be handled. Water measures can be taken to avoid this increase by adjusting aggregate grading and use of super plasticizer. The addition of silica fume will lead to a cohesive mix due to more solid-to-solid contact and will have a lower slump. This reduces bleeding and segregation.
Bleeding and segregation
The effect of silica fume on the rheology of fresh concrete is considered a stabilizing affect in the sense that addition of fine particle to a concrete mix tends to reduce segregation and bleeding. When very fine particles of silica fume are added to concrete the size of flow channel is greatly reduced because these particle are able to find their way into empty spaces between 2 cement grains causing drastic segmentation of bleed water flow and reduce bleeding. Due to increase in the number of solid-to-solid contact, the cohesiveness of the concrete mix is greatly improved when silica fume is added. This makes the concrete highly attractive for pumping, shotcreting as it reduces segregation.
Plastic Shrinkage
Loss of water by evaporation from the surface of concrete or by absorption by aggregate or sub grade is believed to be the reasons of plastic shrinkage, due to which cracks may appear at the surface. Since concrete containing CSF shows little or no bleeding, there are several reports confirming the sensitivity of this concrete to plastic- shrinkage, cracking when exposed to drying conditions at early age. In order to overcome this problem, the surface of concrete must be protected against evaporation as soon as possible after placement. This precaution is a part of the standard concrete curing practice in hot weather.
Properties of hardened silica fume concrete
Creep of concrete is inversely proportional to strength. Since CSF is a highly pozzolanic material, it is expected that the creep of concrete containing CSF will be lower than the corresponding Portland cement concrete a reference concrete made of a calcareous aggregate and normal Portland cement, and a concrete made of the same amount of the aggregate but with 25% (by weight) cement replaced by CSF. The ratio between water to cementations material was 0.435
Examination of the 1- year creep data showed that basic creep strains were similar in both the cases: however, the drying creep strain was about 370 X 10-6 for the reference concrete compared to 300 X 10-6 for the CSF concrete.
Strength characteristic
If CSF is used as an addition, there is no deleterious effect on early strengths (i.e. I- day and 3 day strengths), and a noticeable strength increase is recorded during the 3 to 28 days moist- curing period 30 when most of the pozzolanic reaction takes place. Consequently, the relative strength increase during the 28 to 90 - day period is relatively low. From the results of the investigation reported the addition of 24 kg/m3 CSF to the concrete mixture containing 297 kg/m3 ASTM Type I Portland cement caused a strength increase of about 10% and 20% at 7 and 28 days, respectively; there were no differences in the strength of reference concrete and the CSF - concrete at the test ages I and 2 days.
Three series of both non air- entrained and air- entrained concrete mixtures were designed. The first contained 284kg / m3 of ASTM Type I Portland cement 0.6 ratio between water to cementations materials (i.e., Portland cement + CSF), and 0.5, 10, and 15 % cement replacement replacement by weight with CSF (94 % SiO2, 20 m2/g surface area) The second contained 340kg/m3 Portland cement 0.5 ratio between water to cementations materials, and similar levels of cement replacement with CSF as the first series. The third contained 431 kg /m3 Portland cement, 0.4 ratios between water to cementations materials.
The incorporation of CSF did not result in a significant change in compressive strength at 3 days with concretes of 0.6 and 0.5 ratio of water/ (cement+ CSF); however, the concrete with 0.4 ratio of water / (cement + CSF); showed increase in strength with increasing amount of the fume used in the test (i.e. 5 to 15 % cement replacement)
Regardless of water / (cement + CSF) ratio at 7 days and 28 days the compressive strength of concrete were increased.
All air- entrained concretes, both with and without: CSF, showed strength loss when compared with the corresponding non- air entrained concrete
Post: #3
to get information about the topic "silica fume concrete " full report ppt and related topic refer the link bellow

Important Note..!

If you are not satisfied with above reply ,..Please


So that we will collect data for you and will made reply to the request....OR try below "QUICK REPLY" box to add a reply to this page
Popular Searches: silica fume project, silica concrete, current affairs on silica fume, fumed silica msds, silica fume in trichy, fumed silica india, disadvantages of silica,

Quick Reply
Type your reply to this message here.

Image Verification
Image Verification
(case insensitive)
Please enter the text within the image on the left in to the text box below. This process is used to prevent automated posts.

Possibly Related Threads...
Thread: Author Replies: Views: Last Post
  RAINWATER HARVESTING AND ARTIFICIAL RECHARGE TO GROUND WATER full report project report tiger 11 8,611 17-12-2015 02:13 PM
Last Post: seminar report asees
  Silica Fume Concrete computer science crazy 2 2,974 06-12-2014 06:31 PM
Last Post: seminar report asees
  trenchless technology full report project report tiger 17 15,095 11-07-2014 10:43 PM
Last Post: ahamed fidha
  RAINWATER HARVESTING full report and ppt project topics 11 22,701 27-03-2014 01:14 AM
Last Post: onkarok9294
  skylights full report computer science technology 6 5,027 02-11-2013 01:05 PM
Last Post: sac louis vuitton pas cher
  geopolymer concrete full report project report tiger 11 20,460 16-05-2013 09:34 AM
Last Post: Guest
  green concrete full report project topics 9 34,942 12-03-2013 12:45 PM
Last Post: computer idea
  global warming full report project report tiger 15 23,032 02-03-2013 11:58 AM
Last Post: seminar details
  green buildings for quality living full report project report tiger 5 9,219 16-02-2013 10:44 AM
Last Post: nagarjun ks
  CONSTRUCTION WASTE RECYCLING full report project topics 10 12,255 08-02-2013 10:23 AM
Last Post: seminar details